 Assessing the impact of irradiation-induced defects on the hardening of reactor pressure vessel materials
Tác giả hoặc Nhóm tác giả: Nguyen Ba Vu Chinh et al.
Nơi đăng: International conference on Marine Substainable Development and Innovation; Số: 2023;Từ->đến trang: 11;Năm: 2023
Lĩnh vực: Khoa học công nghệ; Loại: Báo cáo; Thể loại: Quốc tế
TÓM TẮT
ABSTRACT
The most common types of defects that can lead to irradiation-inducedhardening in reactor pressure vessel (RPV) materials are point defects anddislocation loops (DLs). However, their respective contributions to the overallhardening of RPV materials have not been clearly determined. To address thisissue, this study was conducted using iron alloys with equivalent Mn and Nicontent to those used in nuclear RPV in Japan. The study employed transmissionelectron microscopy (TEM), atom probe tomography (APT), andnanoindentation to assess the roles of SCs and DLs in contributing to thehardening behavior of RPV materials. The results indicated that both soluteclusters (SCs), which are formed by the aggregation of point defects, and DLsplay equally important roles in the hardening behavior of RPV materials.However, an in-depth analysis of three-dimensional images using the APTmethod revealed that there may have been errors in evaluating SCs and DLs,leading to double counting when assessing the impact of irradiation-induceddefects on the hardening behavior of RPV materials. These findings highlight theneed for improved accuracy in evaluating these defects to better understand thebehavior of RPV materials under irradiation.